[液体包装复合EAA]EAA3004/EAA•软质包装复合/EAA粘结金属棉麻

EAA 3004 产品说明 

PRIMACOR™ 3004 Copolymer 

产品说明 
PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack 
and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This 
resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR). 
• Excellent draw down and edge stability 
• Excellent product resistance 
• Excellent hot tack, heat seal, toughness 
• High performance sealant or tie layer 
Complies with: 
• U.S. FDA 21 CFR 177.1310(b) 
• EU, No 10/2011 
Consult the regulations for complete details. 
总体 
材料状态 • 已商用：当前有效 
供货地区 • 亚太地区 
机构评级 • EU No 10/2011 • FDA 21 CFR 177.1310 (b) 
形式 • 颗粒料 
物理性能 额定值 单位制 测试方法 
比重 0.938 g/cm³ ASTM D792 
ISO 1183 
熔流率 2 (190°C/2.16 kg) 8.5 g/10 min ASTM D1238 
ISO 1133 
共聚单体含量 3 9.7 % 
机械性能 额定值 单位制 测试方法 
抗张强度 ASTM D638 
ISO 527-2 
屈服, 模压成型 7.93 MPa 
断裂, 模压成型 17.6 MPa 
伸长率 (断裂, 模压成型) 600 % ASTM D638 
ISO 527-2 
热性能 额定值 单位制 测试方法 
维卡软化温度 81.1 °C ASTM D1525 
ISO 306 
溶融温度（DSC） 98.0 °C Internal Method 
挤出 额定值 单位制 测试方法 
熔体温度 260 到 290 °C 
内缩量 (288°C, 25.4 µm) 50.8 mm Internal Method 
较小涂层厚度 10 µm Internal Method 
较小涂层重量 9.8 g/m² Internal Method 
挤压说明 
挤出涂层薄膜的制造条件： 
用于处理此树脂的设备应由耐腐蚀材料制成。建议模具和适配器采用不锈钢和/或双面镀铬或镀镍。 
• 螺杆尺寸：3.5 英寸 (89 mm)；30:1 L/D 
• 模具：30 英寸模具切边至 24 英寸 
• 模具间隙：20 密尔 (0.508 mm) 
• 熔体温度：550°F (288°C) 
• 输出：250 磅/小时 
• 气隙：6 英寸 (152 mm) 
备注 1  一般属性：这些不能被视为规格。 
2  如同在生产时测量的一样。